Abstract This study evaluated the optical method for measuring free total shrinkage using a Digital Single Lens Reflex (DSLR) camera. Eight composites were evaluated, conventional, bulk fill and low-shrinkage: Z100 (3M Oral Care), Gradia Direct Anterior (GC corporation), Spectra Smart (Dentsply), Filtek Z350 XT (3M Oral Care), Aura Bulk Fill (SDI), Vittra APS (FGM), Opus Bulk Fill APS (FGM), and Beautifil II LS (Shofu Inc.). The samples (6 mm diameter and 1.5 mm thick, n = 10) were placed on a polyvinylsiloxane impression material. An image of the uncured sample was captured using a DSLR camera with 105 mm macro lens and a ring flash. Samples were light cured with a 700 mW/cm2 LED light-cure unit for 40s. Post-polymerization images were captured at 2, 10 and 60 min. Projected circumferential areas of the specimens were drawn using the ImageJ software. Volumetric total shrinkage was calculated from the ratio of the areas obtained from pre- and post-curing. Results were analyzed using One-way ANOVA (α = 0.05) and Tukey test. Volumetric total shrinkage values were significantly different among the composite materials (p < .001). The volumetric shrinkage (%) mean and results of Tukey test at 60 min were: Z100: 3.45±0.30 (A); Gradia Direct Anterior: 3.00 ± 0.23 (B); Spectra Smart 2.89 ± 0.35 (B); Filtek Z350 XT: 2.65 ± 0.37 (BC); Aura Bulk Fill: 2.42 ± 0.25 (CD); Vittra APS: 2.14 ± 0.35 (DE); Opus Bulk Fill APS: 1.91 ± 0.24 (E); Beautifil II LS: 1.18 ± 0.16 (F). The optical method using a DSLR camera, was suitable for total shrinkage evaluation and will allow assessment of total shrinkage without the need for specialized equipment.

Abstract: Three-point bending test is the most common mechanical test used for quantifying the biomechanical quality of bone tissue and bone healing in small animals. However, there is a lack of standardization for evaluation of bone repair by cortical perforation. The aim of this study was to determine the influence of bone defect position in the proximal metaphysis of rat tibias during load application and different span configuration on the three-point bending test outcomes. Cortical defects with 1.6 mm diameter were created at a standardized location on the medial surface of 60 tibias of male Wistar rats. The animals were euthanized 7 days after surgery. Five specimens were used to create 3D models for finite element analysis using high-resolution micro-CT images. Two spans (6 and 10mm) and three positions of the bone defect in relation to the load application (upward, frontal and downward) were evaluated experimentally (n = 10) and in finite element analysis (n = 5). Maximum load (N) and stiffness (N/mm) were statistically analyzed with 2-way ANOVA and Tukey test (α = 0.05). The results demonstrated that span and orientation of the bone defect significantly influenced the fracture pattern, stress distribution and force versus displacement relation. Therefore, reliable outcome can be achieved creating the bone defect at 8 mm from the extremity of the proximal epiphysis; placing a 10 mm distance span and downward facing defect position to allow a better distribution of stress and more fracture patterns that reached the bone defect target area with less intra-group variability.

Resumo O objetivo deste estudo foi analisar a influência da presença e tipo de bráquete ortodôntico (metálico ou cerâmico), e a presença de protetor bucal na resposta biomecânica durante impacto. Modelos bidimensionais em estado plano de deformação de paciente com incisivo central superior com overjet positivo acentuado foram criados baseados em tomografia computadorizada, simulando ligamento periodontal, suporte ósseo, tecido gengival, bráquetes ortodônticos (metálico e cerâmico) e o protetor bucal. Análise de elementos finitos não-linear de impacto foi realizada na qual uma esfera de aço atingiu o modelo a 1m/s. A distribuição de tensões (Von Mises e Von Mises modificado) e a deformação foram avaliadas. As distribuições de tensões foram afetadas pela presença e tipo de bráquete. Modelos com bráquete metálico e cerâmico produziram maiores valores de tensões sobre maior área do esmalte vestibular. Modelos com bráquetes cerâmicos geraram maiores tensões do que metálicos. O protetor bucal reduziu as tensões e deformações geradas independentemente do tipo de bráquete. A capacidade de absorção de choques foi de 88.37 e 89.27% para os bráquetes metálicos e cerâmicos, respectivamente. A presença e o tipo de bráquete influenciou a distribuição de tensões e deformações durante o impacto. Bráquetes cerâmicos geraram maiores valores de tensão do que metálicos. Protetor bucal reduziu significativamente os picos de tensão e deformação.

Abstract The aim of this study was to analyze the influence of orthodontic bracket type (metallic or ceramic) and mouthguard on biomechanical response during impact. Two-dimensional plane-strain models of a patient with increased positive overjet of the maxillary central incisor was created based on a CT scan, simulating the periodontal ligament, bone support, gingival tissue, orthodontic brackets (metallic or ceramic) and mouthguard. A nonlinear dynamic impact finite element analysis was performed in which a steel object hit the model at 1 m/s. Stress distributions (Von Mises and Modified Von Mises) and strain were evaluated. Stress distributions were affected by the bracket presence and type. Models with metallic and ceramic bracket had higher stresses over a larger buccal enamel impact area. Models with ceramic brackets generated higher stresses than the metallic brackets. Mouthguards reduced the stress and strain values regardless of bracket type. Mouthguard shock absorption were 88.37% and 89.27% for the metallic and ceramic bracket, respectively. Orthodontic bracket presence and type influenced the stress and strain generated during an impact. Ceramic brackets generated higher stresses than metallic brackets. Mouthguards substantially reduced impact stress and strain peaks, regardless of bracket type.

Abstract Objective To evaluate the influence of three levels of dental structure loss on stress distribution and bite load in root canal-treated young molar teeth that were filled with bulk-fill resin composite, using finite element analysis (FEA) to predict clinical failure. Methodology Three first mandibular molars with extensive caries lesions were selected in teenager patients. The habitual occlusion bite force was measured using gnathodynamometer before and after endodontic/restoration procedures. The recorded bite forces were used as input for patient-specific FEA models, generated from cone-beam computed tomographic (CT) scans of the teeth before and after treatment. Loads were simulated using the contact loading of the antagonist molars selected based on the CT scans and clinical evaluation. Pre and post treatment bite forces (N) in the 3 patients were 30.1/136.6, 34.3/133.4, and 47.9/124.1. Results Bite force increased 260% (from 36.7±11.6 to 131.9±17.8 N) after endodontic and direct restoration. Before endodontic intervention, the stress concentration was located in coronal tooth structure; after rehabilitation, the stresses were located in root dentin, regardless of the level of tooth structure loss. The bite force used on molar teeth after pulp removal during endodontic treatment resulted in high stress concentrations in weakened tooth areas and at the furcation. Conclusion Extensive caries negatively affected the bite force. After pulp removal and endodontic treatment, stress and strain concentrations were higher in the weakened dental structure. Root canal treatment associated with direct resin composite restorative procedure could restore the stress-strain conditions in permanent young molar teeth.

Abstract: Endodontic treatment is a common dental procedure used for treating teeth which the pulp tissue has become irreversibly inflamed or necrotic as a result of the carious process or dental trauma. This procedure which involves mechanical and chemical preparation of root canal may affect several mechanical and physical properties of the tooth structure. The endodontic treatment can also influence the longevity of the rehabilitation of endodontically treated teeth and biomechanics during the oral function. For restoring endodontically treated teeth several factor and clinical decisions should be observed. The decision of the fiberglass post usage and the restorative materials are related to several factors such as the quantity and quality of remaining dental structure, presence of ferrule, post cementation length and final coronal restoration. In this review, the authors will address the effect of the endodontic treatment procedures on canal shape and mechanical properties of a tooth, and also discuss the parameters and the biomechanical principles of root canal treated teeth.

Abstract Polymerization shrinkage stress of resin-based materials have been related to several unwanted clinical consequences, such as enamel crack propagation, cusp deflection, marginal and internal gaps, and decreased bond strength. Despite the absence of strong evidence relating polymerization shrinkage to secondary caries or fracture of posterior teeth, shrinkage stress has been associated with post-operative sensitivity and marginal stain. The latter is often erroneously used as a criterion for replacement of composite restorations. Therefore, an indirect correlation can emerge between shrinkage stress and the longevity of composite restorations or resin-bonded ceramic restorations. The relationship between shrinkage and stress can be best studied in laboratory experiments and a combination of various methodologies. The objective of this review article is to discuss the concept and consequences of polymerization shrinkage and shrinkage stress of composite resins and resin cements. Literature relating to polymerization shrinkage and shrinkage stress generation, research methodologies, and contributing factors are selected and reviewed. Clinical techniques that could reduce shrinkage stress and new developments on low-shrink dental materials are also discussed.